1.2379 Tool Steel Chemical Component Analysis

1.2379 Tool Steel Chemical Component Analysis

 

What is steel?

Steel is an alloy made up of iron with typically a few tenths of a percent of carbon to improve its strength and fracture resistance compared to iron. Many other elements may be present or added. Stainless steels that are corrosion- and oxidation-resistant need typically an additional 11% chromium. Because of its high tensile strength and low cost, steel is used in buildings, infrastructure, tools, ships, trains, cars, machines, electrical appliances, and weapons.

 

What is too steel?

Tool steel is a type of carbon alloy steel that is well-matched for tool manufacturing, such as hand tools or machine dies. Its hardness, resistance to abrasion and ability to retain shape at increased temperatures are the key properties of this material. Tool steel is typically used in a heat treated condition which provides increased hardness.

Types of Tool Steel. The different tool steel grades include:

Water Hardening

Air Hardening

Cold Work tool steel

Hot work tool steel

Oil Hardening

Shock resisting types

 

What is cold work tool steel?

The cold-work tool steels include the O series (oil-hardening), the A series (air-hardening), and the D series (high carbon-chromium). These are steels used to cut or form materials that are at low temperatures. This group possesses high hardenability and wear resistance, and average toughness and heat softening resistance. They are used in production of larger parts or parts that require minimal distortion during hardening. The use of oil quenching and air-hardening helps reduce distortion, avoiding the higher stresses caused by the quicker water quenching. More alloying elements are used in these steels, as compared to the water-hardening class. These alloys increase the steels’ hardenability, and thus require a less severe quenching process and as a result are less likely to crack. They have high surface hardness and are often used to make knife blades. The machinability of the oil hardening grades is high but for the high carbon-chromium types is low.

 

What is 1.2379 steel?

1.2379 steel is a high carbon – high chromium air hardening cold work tool steel, heat treatable to 60-62 HRC. 1.2379 offers excellent wear and abrasion resistance, due to large volumes of carbides in the micro-structure. 1.2379 steel is widely used in long production cold work applications requiring very high wear resistance and high compression strength. It is machinable in the annealed condition, and, like other air hardening tool steels, exhibits minimal distortion in heat treat. 1.2379 steel is available in de-carb free rounds, flats, and squares, as well as ground flat stock and drill rod.

 

What 1.2379 steel used?

Typical applications for 1.2379 steel are blanking, forming, and trim dies, gages, slitting cutters, wear parts, lamination dies, thread rolling dies, drawing dies, rotary cutting dies, knurls, bending dies, gages, shear blades, burnishing tools, rolls, machine parts, master parts, injection screw and tip components, seaming rolls, extrusion dies, tire shredders, scrap choppers, Stamping dies, Forming Dies, Punches, Forming Rolls, Knives, slitters, shear blades, Tools, Scrap choppers, Tyre shredders, etc.

 

1.2379 Steel Chemical Composition Standard:

EN ISO 4957: 2000 Tool steels

 

1.2379 Steel Grade All Grades Comparison:

ASTM;Material No.;DIN;EN

D2;1.2379;X155CrVMo12-1;X160CrMoV121

 

1.2379 Steel Chemical Composition(%)

C Si Mn P S Cr Mo V
1.40-1.60 0.10-0.60 0.10-0.60 0.030 max 0.030 max 11.0-13.0 0.70-1.20 0.50-1.10

 

1.2379 Steel Elements Analysis:

Carbon-C

Carbon is inseparable from steel and is therefore usually not defined as alloying constituent. Carbon is the most important element for the majority of steels and has the strongest influence on their properties.

 

Vanadium-V

Vanadium refines the primary grain and thus the as cast structure. It is a strong carbide forming element, thus causing an increase in wear resistance, edge holding properly and high-temperature strength. It is therefore a preferred alloying constituent in high-speed steels, hot work tool steels and high-temperature steels.

 

Chromium-Cr

Chromium makes steel oil and air hardenable. By lowering the critical cooling rate necessary for the formation of martensite, it increases hardenability and thus improves heat treating properties while at the same time it reduces impact strength. Chromium is a strong carbide former.

 

Manganese-Mn

Manganese has a deoxidizing effect. It combines with sulphur to form manganese sulphides and hus lowers the untavourable effect of iron sulphides. This is of particular importance for free- cuting steels because itreduces the risk of red shortness.

 

Molybdenum-Mo

Molybdenum is mostly added together with other alloying elements. By reducing the critical cooling rate, it improves hardenability Mn reduces to a large extent temper brittleness, e.g. in CrNi and Mn steels, and promotes fine-grain formation.

 

Nickel-Ni

In constructional steels, Ni causes an increase of impact strength, even at subzero temperatures is therefore added to case-hardening steels, heat treatable steels and steels intended for low temperature service to increase theirtoughness properties All transformation points (A1-A4) are lowered by nickel.

 

Aluminum-Al

Aluminum is the strongest and most common used deoxidizing and dentriding agent. It has therefor a favorable effect on the intensivity to ageing and it promotes a fine grain formation, when added in small amounts.

 

Copper-Cu

Copper is only added to a few steel grades, because it builds up below the oxide layer and produces high surface sensitivity in hot forming operations due to penetration into the grain boundary.

 

Silicon – Si

Silicon has a deoxidizing effect. It promotes graphite precipitation and narrows subtantially the gamma-range. It increases strength and wear resistance (heat treatable Si-Mn steels). Silicon causes a considerable increase of the elastic limit and is therefore most suitable as alloying constituent in spring steels. Owing to its ability to improve substantially the resistance to scaling, Si is added to heat resisting steels. Its contents are, however, limited, as it impairs the hot and cold forming properties.

 

Sulphur – S

Among all trace elements, sulphur produces the most serious segregations. Iron sulphide leads to red shortness because the low melting sulphide eutectics surround the grains like a net, resulting in a low coherence of the latter and in breaking up of grain boundaries during hot forming. This phenomenon is intensified by the effect of oxygen.

 

How 1.2379 steel produce?

Electric Arc Furnace (EAF) Melting: This process is also known as primary melting. It is based on the melting of metal chips which are obtained from milling processes and suppliers. Basically, EAF melting uses leftovers of different metal processing methods. Electric arc furnace melting is widely used because the production costs are low. Still some extra treatment may be needed to achieve the highest possible quality and properties. An example of this is annealing to prevent cracking.

Electroslag Refining (ESR): Electroslag refining is also known as electroslag remelting. Throughout the process, the metal is melted progressively. The resulting ingots have good surface quality without notable imperfections.

Fushun Special Steel LTD CO

Fushun Metal is a large special steel manufacuter and supplie. We are metal experts and have been providing quality customer service and products since 1998.

 

At Fushun Metal, we supply a wide range of metals for a variety of applications. Our products/stock includes: stainless steel, alloy steel, spring steel, tool steel, high speed steel, mould steel, nickel alloy.

 

Our hot rolled and cold rolled steel is available in a wide range of shapes including: bars, tubes, sheets and plates. We can cut metal to your exact specifications.

 

Send your inquiry information to us and get a free quotation today!

 

About Us

Founded in 1998, FuShun covers an area of 3000 square meters, annual sales volume of 20000 tons. We are engaged in the manufacture and export of Tool Steel, Nickel Alloy, Stainless Steel and other special steel products…,View more content About Me.

Get A Free Quote!

Fushun TEL: +86-731-89903933

Fushun FAX: +86-731-89853933

General Manager: Ms. Florence Tang

Whatsapp/Phone/WeChat:+86-13319591838

Find your steel grade and get a quote today.

NOW Send Your Inquiry To : info@fushunspecialsteel.com

Whatsapp:+86-18692275455

x